Amine-pillared Nanosheet Adsorbents for CO2 Capture Applications PDF Download

Author: Hui Jiang
Publisher:
ISBN:
Category : Amines
Languages : en
Pages : 52

Get Book Here

Book Description
Amine-functionalized solid adsorbents have gained attention within the last decade for their application in carbon dioxide capture, due to their many advantages such as low energy cost for regeneration, tunable structure, elimination of corrosion problems, and additional advantages. However, one of the challenges facing this technology is to accomplish both high CO2 capture capacity along with high CO2 diffusion rates concurrently. Current amine-based solid sorbents such as porous materials similar to SBA-15 have large pores diffusion entering molecules; however, the pores become clogged upon amine inclusion. To meet this challenge, our group's solution involves the creation of a new type of material which we are calling-amino-pillared nanosheet (APN) adsorbents which are generated from layered nanosheet precursors. These materials are being proposed because of their unique lamellar structure which exhibits ability to be modified by organic or inorganic pillars through consecutive swelling and pillaring steps to form large mesoporous interlayer spaces. After the expansion of the layer space through swelling and pillaring, the large pore space can be functionalized with amine groups. This selective functionalization is possible by the choice of amine group introduced. Our choice, large amine molecules, do not access the micropore within each layer; however, either physically or chemically immobilized onto the surface of the mesoporous interlayer space between each layer. The final goal of the research is to investigate the ability to prepare APN adsorbents from a model nanoporous layered materials including nanosheets precursor material MCM-22(P) and nanoporous layered silicate material AMH-3. MCM-22(P) contains 2-dimensional porous channels, 6 membered rings (MB) openings perpendicular to the layers and 10 MB channels in the plane of the layers.1 However, the transport limiting openings (6 MB) to the layers is smaller than CO2 gas molecules.2,3 In contrast, AMH-3 has 3D microporous layers with 8 MB openings in the plane of the layers, as well as perpendicular to the layers, which are larger than CO2 molecules. Based on the structure differences between nanosheets precursor material MCM-22(P) and nanoporous layered silicate material AMH-3, the latter might be more suitable for CO2 capturer application as an APN candidate material. However, none of the assumptions above have been approved experimentally. In this study, the influence of the amine loading on adsorption capacity and kinetics of adsorption for the mixed porosity material pillared MCM-22 (P) (also called MCM-36) is studied systematically, in order to determine a potential route to achieve a final material with both high amine loading and high adsorption capacity. We first synthesized MCM-22(P), followed by swelling and pillaring to create MCM-36. Polymeric amines such as polyethylenimine (PEI) are used as an organic component of the supported amine adsorbents, with varying polymer loadings within the adsorbents used. The kinetics and diffusion properties of carbon dioxide capture on a MCM-36 pillared material impregnated with amine containing Polyethylenimine polymers has been investigated. It was determined that the introduction of amine polymer cannot be used to improve the capture capacity of the support over that of the bare material, due to the fact that with the addition of a high loading of amine polymer the large pore diffusion channels become impossible for carbon dioxide molecules to diffuse through. This sets an upper limit to the capture capacity of polymer impregnated MCM-36 for carbon dioxide which does not surpass that for the initial bare material, and greatly reduces the utility of using this sort of amine-solid adsorbent for carbon capture plans in the future.