Denting is a form of damage that results from the rapid, linear growth of magnetite on carbon steel tube support plates in tube-to-support plate crevices. The pressure of the corrosion products distorts the tubes as well as the support plates. Although denting was first thought to be confined to those recirculating steam generators that had been converted from phosphate to AVT, it has now also been observed in plants still on phosphate, as well as in some that started on AVT. In some units, slightly abnormal eddy current signals have been observed at the top of tube sheets. No denting has been observed so far in the B and W once-through steam generators. In all, some 14 plants are affected. Inconel 600 tube defects and leaks were first observed at Surry and Turkey Point, which were severely dented. The cracks originated from the primary side, and were found to be caused by primary side stress corrosion cracking of highly strained tubing. Some minor leaks have subsequently occurred in a few other steam generators. Suggestions are included of work to elucidate the quantitative aspects of stress corrosion cracking.
Denting of Inconel Steam Generator Tubes in Pressurized Water Reactors. Final Report
Author:
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Denting is a form of damage that results from the rapid, linear growth of magnetite on carbon steel tube support plates in tube-to-support plate crevices. The pressure of the corrosion products distorts the tubes as well as the support plates. Although denting was first thought to be confined to those recirculating steam generators that had been converted from phosphate to AVT, it has now also been observed in plants still on phosphate, as well as in some that started on AVT. In some units, slightly abnormal eddy current signals have been observed at the top of tube sheets. No denting has been observed so far in the B and W once-through steam generators. In all, some 14 plants are affected. Inconel 600 tube defects and leaks were first observed at Surry and Turkey Point, which were severely dented. The cracks originated from the primary side, and were found to be caused by primary side stress corrosion cracking of highly strained tubing. Some minor leaks have subsequently occurred in a few other steam generators. Suggestions are included of work to elucidate the quantitative aspects of stress corrosion cracking.
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Denting is a form of damage that results from the rapid, linear growth of magnetite on carbon steel tube support plates in tube-to-support plate crevices. The pressure of the corrosion products distorts the tubes as well as the support plates. Although denting was first thought to be confined to those recirculating steam generators that had been converted from phosphate to AVT, it has now also been observed in plants still on phosphate, as well as in some that started on AVT. In some units, slightly abnormal eddy current signals have been observed at the top of tube sheets. No denting has been observed so far in the B and W once-through steam generators. In all, some 14 plants are affected. Inconel 600 tube defects and leaks were first observed at Surry and Turkey Point, which were severely dented. The cracks originated from the primary side, and were found to be caused by primary side stress corrosion cracking of highly strained tubing. Some minor leaks have subsequently occurred in a few other steam generators. Suggestions are included of work to elucidate the quantitative aspects of stress corrosion cracking.
Denting of Inconel Steam Generator Tubes in Pressurized Water Reactors
Author: Daniel Van Rooyen
Publisher:
ISBN:
Category : Nuclear reactors
Languages : en
Pages : 44
Book Description
Publisher:
ISBN:
Category : Nuclear reactors
Languages : en
Pages : 44
Book Description
Steam Generator Tube Integrity Program
Author: Milton Vagins
Publisher:
ISBN:
Category : Pressurized water reactors
Languages : en
Pages : 148
Book Description
Publisher:
ISBN:
Category : Pressurized water reactors
Languages : en
Pages : 148
Book Description
Steam Generator Tube Integrity Program
Author: J. M. Alzheimer
Publisher:
ISBN:
Category : Pressurized water reactors
Languages : en
Pages : 284
Book Description
Publisher:
ISBN:
Category : Pressurized water reactors
Languages : en
Pages : 284
Book Description
Energy Research Abstracts
Author:
Publisher:
ISBN:
Category : Power resources
Languages : en
Pages : 548
Book Description
Publisher:
ISBN:
Category : Power resources
Languages : en
Pages : 548
Book Description
Structural Materials in Nuclear Power Systems
Author: J. T. Adrian Roberts
Publisher: Springer Science & Business Media
ISBN: 1468471945
Category : Technology & Engineering
Languages : en
Pages : 493
Book Description
In recent years the effort devoted to assuring both the safety and reliability of commercial nuclear fission power reactors has markedly increased. The incentives for performing this work are large since the resulting im provement in plant productivity translates into lower fuel costs and, more importantly, reduced reliance on imported oil. Reliability and availability of nuclear power plants, whether fission or fusion, demand that more attention be focused on the behavior of materials. Recent experiences with fission power indicate that the basic properties of materials, which categorize their reliable behavior under specified conditions, need reinforcement to assure trouble-free operation for the expected service life. The pursuit of additional information con tinues to demand a better understanding of some of the observed anom alous behavior, and of the margin of resistance of materials to unpre dictable service conditions. It is also apparent that, next to plasma heating and confinement, materials selection represents the most serious chal lenge to the introduction of fusion power. The recognition of the importance of materials performance to nu clear plant performance has sustained a multimillion dollar worldwide research and development effort that has yielded significant results, both in quantification of the performance limits of materials in current use and the development and qualification of new materials. Most of this infor mation appears in the open literature in the form of research reports, journal articles, and conference proceedings.
Publisher: Springer Science & Business Media
ISBN: 1468471945
Category : Technology & Engineering
Languages : en
Pages : 493
Book Description
In recent years the effort devoted to assuring both the safety and reliability of commercial nuclear fission power reactors has markedly increased. The incentives for performing this work are large since the resulting im provement in plant productivity translates into lower fuel costs and, more importantly, reduced reliance on imported oil. Reliability and availability of nuclear power plants, whether fission or fusion, demand that more attention be focused on the behavior of materials. Recent experiences with fission power indicate that the basic properties of materials, which categorize their reliable behavior under specified conditions, need reinforcement to assure trouble-free operation for the expected service life. The pursuit of additional information con tinues to demand a better understanding of some of the observed anom alous behavior, and of the margin of resistance of materials to unpre dictable service conditions. It is also apparent that, next to plasma heating and confinement, materials selection represents the most serious chal lenge to the introduction of fusion power. The recognition of the importance of materials performance to nu clear plant performance has sustained a multimillion dollar worldwide research and development effort that has yielded significant results, both in quantification of the performance limits of materials in current use and the development and qualification of new materials. Most of this infor mation appears in the open literature in the form of research reports, journal articles, and conference proceedings.
Energy Research Abstracts
Author:
Publisher:
ISBN:
Category : Power resources
Languages : en
Pages : 692
Book Description
Publisher:
ISBN:
Category : Power resources
Languages : en
Pages : 692
Book Description
Monthly Catalog of United States Government Publications
Author: United States. Superintendent of Documents
Publisher:
ISBN:
Category : Government publications
Languages : en
Pages : 1546
Book Description
February issue includes Appendix entitled Directory of United States Government periodicals and subscription publications; September issue includes List of depository libraries; June and December issues include semiannual index
Publisher:
ISBN:
Category : Government publications
Languages : en
Pages : 1546
Book Description
February issue includes Appendix entitled Directory of United States Government periodicals and subscription publications; September issue includes List of depository libraries; June and December issues include semiannual index
Monthly Catalogue, United States Public Documents
Author:
Publisher:
ISBN:
Category : Government publications
Languages : en
Pages : 1094
Book Description
Publisher:
ISBN:
Category : Government publications
Languages : en
Pages : 1094
Book Description
ERDA Energy Research Abstracts
Author:
Publisher:
ISBN:
Category :
Languages : en
Pages : 724
Book Description
Publisher:
ISBN:
Category :
Languages : en
Pages : 724
Book Description