Investigation of Fatigue-crack Growth Under Simple Variable-amplitude Loading PDF Download
Are you looking for read ebook online? Search for your book and save it on your Kindle device, PC, phones or tablets. Download Investigation of Fatigue-crack Growth Under Simple Variable-amplitude Loading PDF full book. Access full book title Investigation of Fatigue-crack Growth Under Simple Variable-amplitude Loading by C. M. Hudson. Download full books in PDF and EPUB format.
Author: C. M. Hudson
Publisher:
ISBN:
Category : Airframes
Languages : en
Pages : 28
Get Book Here
Book Description
VARIABLE-AMPLITUDE FATIGUE-CRACK-GROWTH TESTS WERE CONDUCTED ON SIMPLE SHEET SPECIMENS MADE OF 7075-T6 ALUMINUM ALLOY. THE NUMBERS AND THE AMPLITUDES OF THE HIGH-LOAD CYCLES APPLIED IN THESE TESTS WERE SYSTEMATICALLY VARIED TO STUDY THEIR EFFECTS ON SUBSEQUENT LOW-LOAD FATIGUE-CRACK GROWTH. THE HIGH-LOAD CYCLES CONSISTENTLY DELAYED SUBSEQUENT FATIGUE-CRACK GROWTH AT LOWER LOAD LEVELS. FOR A GIVEN LOW-LOAD LEVEL, THE HIGHER THE PRECEDING HIGH-LOAD LEVEL WAS, THE GREATER THE DELAY IN CRACK PROPAGATION. FURTHERMORE, THE DELAY IN CRACK GROWTH INCREASED WITH INCREASING NUMBERS OF HIGH-LOAD CYCLES UP TO A LIMIT. ONE HIGH-LOAD CYCLE CAUSED APPROXIMATELY ONE-FOURTH OF THE MAXIMUM DELAY, AND TEN HIGH-LOAD CYCLES CAUSED APPROXIMATELY ONE-HALF OF THE MAXIMUM DELAY. THESE DELAYS PROBABLY RESULTED FROM RESIDUAL COMPRESSIVE STRESSES GENERATED IN THE MATERIAL IMMEDIATELY AHEAD OF THE CRACK TIP DURING THE APPLICATION OF THE HIGH-LOAD CYCLES. ELECTRON FRACTOGRAPHIC STUDIES SHOWED THAT A GIVEN STRESS LEVEL, FATIGUE CRACKS PROPAGATED MORE SLOWLY IMMEDIATELY AFTER THE APPLICATION OF A HIGH-LOAD CYCLE THAN THEY DID IMMEDIATELY BEFORE ITS APPLICATION. THIS LOWER CRACK-GROWTH RATE IS CONSISTENT WITH THE DELAY IN CRACK GROWTH OBSERVED ON THE MACROSCOPIC LEVEL.
Author: C. M. Hudson
Publisher:
ISBN:
Category : Airframes
Languages : en
Pages : 28
Get Book Here
Book Description
VARIABLE-AMPLITUDE FATIGUE-CRACK-GROWTH TESTS WERE CONDUCTED ON SIMPLE SHEET SPECIMENS MADE OF 7075-T6 ALUMINUM ALLOY. THE NUMBERS AND THE AMPLITUDES OF THE HIGH-LOAD CYCLES APPLIED IN THESE TESTS WERE SYSTEMATICALLY VARIED TO STUDY THEIR EFFECTS ON SUBSEQUENT LOW-LOAD FATIGUE-CRACK GROWTH. THE HIGH-LOAD CYCLES CONSISTENTLY DELAYED SUBSEQUENT FATIGUE-CRACK GROWTH AT LOWER LOAD LEVELS. FOR A GIVEN LOW-LOAD LEVEL, THE HIGHER THE PRECEDING HIGH-LOAD LEVEL WAS, THE GREATER THE DELAY IN CRACK PROPAGATION. FURTHERMORE, THE DELAY IN CRACK GROWTH INCREASED WITH INCREASING NUMBERS OF HIGH-LOAD CYCLES UP TO A LIMIT. ONE HIGH-LOAD CYCLE CAUSED APPROXIMATELY ONE-FOURTH OF THE MAXIMUM DELAY, AND TEN HIGH-LOAD CYCLES CAUSED APPROXIMATELY ONE-HALF OF THE MAXIMUM DELAY. THESE DELAYS PROBABLY RESULTED FROM RESIDUAL COMPRESSIVE STRESSES GENERATED IN THE MATERIAL IMMEDIATELY AHEAD OF THE CRACK TIP DURING THE APPLICATION OF THE HIGH-LOAD CYCLES. ELECTRON FRACTOGRAPHIC STUDIES SHOWED THAT A GIVEN STRESS LEVEL, FATIGUE CRACKS PROPAGATED MORE SLOWLY IMMEDIATELY AFTER THE APPLICATION OF A HIGH-LOAD CYCLE THAN THEY DID IMMEDIATELY BEFORE ITS APPLICATION. THIS LOWER CRACK-GROWTH RATE IS CONSISTENT WITH THE DELAY IN CRACK GROWTH OBSERVED ON THE MACROSCOPIC LEVEL.
Author: J. Petit
Publisher: Springer
ISBN:
Category : Technology & Engineering
Languages : en
Pages : 422
Get Book Here
Book Description
Author: J. Schijve
Publisher: Springer Science & Business Media
ISBN: 1402068085
Category : Science
Languages : en
Pages : 627
Get Book Here
Book Description
Fatigue of structures and materials covers a wide scope of different topics. The purpose of the present book is to explain these topics, to indicate how they can be analyzed, and how this can contribute to the designing of fatigue resistant structures and to prevent structural fatigue problems in service. Chapter 1 gives a general survey of the topic with brief comments on the signi?cance of the aspects involved. This serves as a kind of a program for the following chapters. The central issues in this book are predictions of fatigue properties and designing against fatigue. These objectives cannot be realized without a physical and mechanical understanding of all relevant conditions. In Chapter 2 the book starts with basic concepts of what happens in the material of a structure under cyclic loads. It illustrates the large number of variables which can affect fatigue properties and it provides the essential background knowledge for subsequent chapters. Different subjects are presented in the following main parts: • Basic chapters on fatigue properties and predictions (Chapters 2–8) • Load spectra and fatigue under variable-amplitude loading (Chapters 9–11) • Fatigue tests and scatter (Chapters 12 and 13) • Special fatigue conditions (Chapters 14–17) • Fatigue of joints and structures (Chapters 18–20) • Fiber-metal laminates (Chapter 21) Each chapter presents a discussion of a speci?c subject.
Author: Ralph Ivan Stephens
Publisher: ASTM International
ISBN:
Category : Alloys
Languages : en
Pages : 345
Get Book Here
Book Description
Author: D. F. Bryan
Publisher: ASTM International
ISBN: 9780803107205
Category : Technology & Engineering
Languages : en
Pages : 256
Get Book Here
Book Description
Author:
Publisher:
ISBN:
Category :
Languages : en
Pages : 546
Get Book Here
Book Description
Author: Gert Heinrich
Publisher: Springer Nature
ISBN: 3030689204
Category : Technology & Engineering
Languages : en
Pages : 491
Get Book Here
Book Description
The book summarizes recent international research and experimental developments regarding fatigue crack growth investigations of rubber materials. It shows the progress in fundamental as well as advanced research of fracture investigation of rubber material under fatigue loading conditions, especially from the experimental point of view. However, some chapters will describe the progress in numerical modeling and physical description of fracture mechanics and cavitation phenomena in rubbers. Initiation and propagation of cracks in rubber materials are dominant phenomena which determine the lifetime of these soft rubber materials and, as a consequence, the lifetime of the corresponding final rubber parts in various fields of application. Recently, these phenomena became of great scientific interest due to the development of new experimental methods, concepts and models. Furthermore, crack phenomena have an extraordinary impact on rubber wear and abrasion of automotive tires; and understanding of crack initiation and growth in rubbers will help to support the growthing number of activities and worldwide efforts of reduction of tire wear losses and abrasion based emissions.
Author:
Publisher:
ISBN:
Category : Aeronautics
Languages : en
Pages : 702
Get Book Here
Book Description
Author: Raghavan Srinivasan
Publisher: John Wiley & Sons
ISBN: 1118013352
Category : Technology & Engineering
Languages : en
Pages : 449
Get Book Here
Book Description
Fatigue of Materials covers a broad spectrum of topics that represent the truly diverse nature of the subject that has grown to become a key area of scientific and applied research. Constituting an international forum for the materials industry, the book provides the perspectives of operators, engineers, and researchers regarding all aspects of current and emerging technologies for materials.
Author: L. F. Impellizzeri
Publisher: ASTM International
ISBN:
Category : Technology & Engineering
Languages : en
Pages : 242
Get Book Here
Book Description