Evaluation of Corrosion Protection Methods for Reinforced Concrete Highway Structures PDF Download
Are you looking for read ebook online? Search for your book and save it on your Kindle device, PC, phones or tablets. Download Evaluation of Corrosion Protection Methods for Reinforced Concrete Highway Structures PDF full book. Access full book title Evaluation of Corrosion Protection Methods for Reinforced Concrete Highway Structures by Jennifer L. Kepler. Download full books in PDF and EPUB format.
Author: Jennifer L. Kepler
Publisher:
ISBN:
Category : Concrete bridges
Languages : en
Pages : 244
Get Book Here
Book Description
Since the 1970s, research projects and field studies have been conducted on different methods for protecting reinforced concrete bridges from corrosion damage. The methods include alternative reinforcement and slab design, barrier methods, electrochemical methods, and corrosion inhibitors. Each method and its underlying principles are described, performance results of laboratory and/or field trials are reviewed, and systems are evaluated based on the results of the trials. Using performance results from the studies and costs obtained from transportation agencies, an economic analysis is used to estimate the cost of each system over a 75-year economic life using discount rates of 2%, 4% and 6%.
Author: Jennifer L. Kepler
Publisher:
ISBN:
Category : Concrete bridges
Languages : en
Pages : 244
Get Book Here
Book Description
Since the 1970s, research projects and field studies have been conducted on different methods for protecting reinforced concrete bridges from corrosion damage. The methods include alternative reinforcement and slab design, barrier methods, electrochemical methods, and corrosion inhibitors. Each method and its underlying principles are described, performance results of laboratory and/or field trials are reviewed, and systems are evaluated based on the results of the trials. Using performance results from the studies and costs obtained from transportation agencies, an economic analysis is used to estimate the cost of each system over a 75-year economic life using discount rates of 2%, 4% and 6%.
Author: Habib Tabatabai
Publisher:
ISBN:
Category : Concrete bridges
Languages : en
Pages : 376
Get Book Here
Book Description
Author: Yunping Xi
Publisher:
ISBN:
Category : Concrete bridges
Languages : en
Pages : 166
Get Book Here
Book Description
Corrosion of reinforced concrete structures has been a significant problem for many state and transportation agencies since the application of deicing salts was introduced. Much research has been conducted to develop corrosion protection systems that can prolong the life span of reinforced concrete structures. The Colorado Department of Transportation (CDOT) has several routine and experimental measures to prevent corrosion of the rebar including epoxy-coated rebar, calcium nitrite admixture, organic corrosion inhibitors, a thick cover of quality concrete, and a waterproofing membrane covered by an asphalt overlay. An extensive literature review was performed to collect information on various corrosion protection systems that have been used in the U.S. and around the world. Current CDOT practices in terms of corrosion protection measures were reviewed. A draft inspection plan for Colorado's bridge structures was proposed.
Author: El Kacimi, Younes
Publisher: IGI Global
ISBN: 1799827771
Category : Technology & Engineering
Languages : en
Pages : 304
Get Book Here
Book Description
Metals are used at an extremely high rate in the industrial and manufacturing fields. Exemplary properties including strength and ductility have made this material highly dynamic; however, the risk of corrosion remains a vital issue. The study of corrosion prevention has attracted interest from researchers and professionals as new technologies are emerging that can assist in the prevention of material destruction. However, research is lacking on the application of these protective technologies within specific fields. New Challenges and Industrial Applications for Corrosion Prevention and Control provides emerging research exploring the theoretical and practical aspects of protective methods against corrosion and the implementation of these techniques within a wide span of professional disciplines. Featuring coverage on a broad range of topics such as molecular modeling, surface treatments, and biomaterials, this book is ideally designed for engineers, industrial chemists, material scientists, researchers, engineers, academicians, practitioners, and students seeking current research on the technological advancements in corrosion protection in various professional scopes.
Author: E. Escalante
Publisher:
ISBN:
Category : Bridges, Concrete
Languages : en
Pages : 32
Get Book Here
Book Description
Author: John P. Broomfield
Publisher: CRC Press
ISBN: 1000822486
Category : Technology & Engineering
Languages : en
Pages : 305
Get Book Here
Book Description
Corrosion of Steel in Concrete: Understanding, Investigation and Repair is a guide for designing, constructing and maintaining reinforced concrete structures, such as buildings and bridges which are subject to reinforcement corrosion. It presents the basics of theory and practice in steel corrosion in concrete and reviews the latest research and developments, such as progress on measuring the corrosion threshold for chloride-induced corrosion. This third edition compares the currently proliferating major national and international standards and guidance documents. New developments are considered, such as hybrid anodes for electrochemical treatment and the latest research and developments in assessment, such as the use of ground penetrating radar to measure the chloride content of the concrete cover. It overhauls coverage of electrochemical repair and rehabilitation techniques and outlines recent innovations in structural repair and construction and investigates their implications for durability. The book is ideal for practitioners and graduate students in structural engineering and concrete technology.
Author: Ali Akbar Sohanghpurwala
Publisher: Transportation Research Board National Research
ISBN:
Category : Science
Languages : en
Pages : 76
Get Book Here
Book Description
Author: M Raupach
Publisher: Woodhead Publishing
ISBN: 1845692284
Category : Technology & Engineering
Languages : en
Pages : 337
Get Book Here
Book Description
Given the widespread use of reinforced concrete in infrastructure, understanding the corrosion of this material is of major importance. As a result there has been a wealth of research into catalysts, inhibitors and effective means of monitoring the rate of corrosion. Corrosion of reinforcement in concrete: mechanisms, monitoring, inhibitors and rehabilitation techniques summarises some of the most significant research and its implications.The book begins by reviewing findings from various experiments designed to test the corrosion rate of metals induced by a range of factors. Later chapters discuss techniques for monitoring and testing for corrosion. The book concludes by assessing important methods of prevention, including corrosion inhibitors, protective coatings and electrochemical methods for protection, together with rehabilitation procedures for susceptible structures.Filled with practical examples and written by a distinguished team of international contributors, Corrosion of reinforcement in concrete: mechanisms, monitoring, inhibitors and rehabilitation techniques is an essential reference for civil engineers using reinforced concrete. Summarises research into catalysts, inhibitors and effective means of monitoring the rate of corrosion Concludes by assessing important methods of prevention
Author: Jerzy Zemajtis
Publisher:
ISBN:
Category : Concrete bridges
Languages : en
Pages : 152
Get Book Here
Book Description
The application of a mineral admixture or a combination of a mineral admixture with corrosion inhibitor are the methods used for the corrosion protection for reinforced concrete bridges. The results of a 1.5-year study on evaluation of three concretes with fly ash, slag cement (SC), and silica fume (SF) and one concrete with silica fume and a corrosion inhibitor (SFD) are presented. The specimens were built to simulate four exposure conditions typical for concrete bridges located in the coastal region or inland where deicing salts are used. The exposure conditions were horizontal, vertical, tidal, and immersed zones. The specimens were kept inside the laboratory and were exposed to weekly ponding cycles of 6% sodium chloride solution by weight. In addition, cover depth measurements from 21 bridge decks and chloride data from 3 bridge decks were used, together with laboratory data, in modeling the service lives of investigated corrosion protection methods. The methods used to assess the condition of the specimens included chloride concentration measurements, corrosion potentials, and corrosion rates (3LP). Additionally, visual observations were performed for identification of rust stains and cracking on concrete surfaces. The results of chloride testing indicate that the amount of chlorides present at the bar level is more than sufficient to initiate corrosion. Chloride and rapid permeability data demonstrate that for low permeable (LP) concretes there appears to be significant difference both in a rate of chloride ingress and in the diffusion coefficients in comparison to the controls. Corrosion potentials agree with corrosion rates and suggest the possibility of an active corrosion process development on control specimens during indoor exposure. The structural cracks that were observed in some specimens appeared to have no influence on the corrosion development on the bars in the vicinity of the these cracks. It was concluded that the silicone and duct tape protection was adequate. The cracking, other than structural, appeared to be related to the reinforcing steel corrosion, except the cracks in the horizontal zone of the specimen with slag cement which were probably caused by the subsidence cracking. The least number of cracks was observed on the SF and SFD specimens. Modeling the time as a function of probability of the end of functional service life (EFSL) was presented. It has been shown that the distributions of surface concentrations of chloride ions (CO) and diffusion constants (DC) are key elements in the model. Model predictions show that the LP concretes provide much better level of protection against moisture and chlorides than the A4 concrete alone. Application of a corrosion inhibitor causes an elevation of the chloride threshold resulting in an additional increase in time to EFSL. Recommendations are to continue monitoring until cracking has occurred in all specimens to a greater extent to better estimate the service lives of LP concretes than is presently known in the construction of concrete bridge components in Virginia. The specimens with LP concretes and one control (continuous reinforcement in the legs) should be taken to the Hampton Road North Tunnel Island and placed in the brackish water to a depth of the immersed zone at low tide for further exposure to chloride. The other control (non-continuous reinforcement in the legs) should remain in an outdoor exposure in Southwest Virginia like the Civil Engineering Materials Research Laboratory in Blacksburg, Virginia. Also more field studies are needed to better estimate distributions of surface chloride concentration and diffusion coefficient of Virginia bridge decks, and to confirm predicted times to EFSL for LP concretes.
Author: J. L. Smith
Publisher:
ISBN:
Category : Concrete bridges
Languages : en
Pages : 90
Get Book Here
Book Description
Salt-induced reinforcing steel corrosion in concrete bridges has undoubtedly become a considerable economic burden to many State and local transportation agencies. Since the iron in the steel has a natural tendency to revert eventually to its most stable oxide state, this problem will, unfortunately, still be with us, but to a much lesser degree due to the use of various corrosion protection strategies currently used in new construction. The adoption of corrosion protection measures in new construction, such as the use of good design and construction practices, adequate concrete cover depth, low-permeability concrete, corrosion inhibitors, and coated reinforcing steel is significantly reducing the occurrence of reinforcing steel corrosion in new bridges.