IN THE SOLUTION TREATED AND AGED CONDITION, Ti4Al-3Mo-1V has a higher ultimate strength than does Ti-2.5Al-16V, but the two alloys are about even in yield strength and elongation. In the solution-treated condition, Ti-4Al-3Mo-1V is unquestionably stronger than Ti-2.5Al-16V. These conclusions are independent of producer. There is not much difference in the same alloy produced by different companies. The alloys developed under the Titanium-Alloy Sheet-Rolling Program would not endure the most critical interpretation of release property specifications. On the other hand, these alloys come reasonably close to specifications. A complete set of release property specifications is available only for specimens that have been solution treated and aged. Such specimens do not all exhibit the desired ultimate and yield strength, but the percentage of rejects is small enough to be encouraging. (Author).
Statistical Analysis of Tensile Properties of Heat-treated Ti-4A1-3Mo-1V and Ti-2.5A1-16V Sheet
Author: G. H Beatty
Publisher:
ISBN:
Category : Metals
Languages : en
Pages : 54
Book Description
IN THE SOLUTION TREATED AND AGED CONDITION, Ti4Al-3Mo-1V has a higher ultimate strength than does Ti-2.5Al-16V, but the two alloys are about even in yield strength and elongation. In the solution-treated condition, Ti-4Al-3Mo-1V is unquestionably stronger than Ti-2.5Al-16V. These conclusions are independent of producer. There is not much difference in the same alloy produced by different companies. The alloys developed under the Titanium-Alloy Sheet-Rolling Program would not endure the most critical interpretation of release property specifications. On the other hand, these alloys come reasonably close to specifications. A complete set of release property specifications is available only for specimens that have been solution treated and aged. Such specimens do not all exhibit the desired ultimate and yield strength, but the percentage of rejects is small enough to be encouraging. (Author).
Publisher:
ISBN:
Category : Metals
Languages : en
Pages : 54
Book Description
IN THE SOLUTION TREATED AND AGED CONDITION, Ti4Al-3Mo-1V has a higher ultimate strength than does Ti-2.5Al-16V, but the two alloys are about even in yield strength and elongation. In the solution-treated condition, Ti-4Al-3Mo-1V is unquestionably stronger than Ti-2.5Al-16V. These conclusions are independent of producer. There is not much difference in the same alloy produced by different companies. The alloys developed under the Titanium-Alloy Sheet-Rolling Program would not endure the most critical interpretation of release property specifications. On the other hand, these alloys come reasonably close to specifications. A complete set of release property specifications is available only for specimens that have been solution treated and aged. Such specimens do not all exhibit the desired ultimate and yield strength, but the percentage of rejects is small enough to be encouraging. (Author).
Statistical Analysis of Tensile Properties of Heat-treated Ti-4Al-3Mo-IV and Ti-2.5Al-16V Sheet
Author: G. H. Beatty
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Publisher:
ISBN:
Category :
Languages : en
Pages :
Book Description
Statistical Analysis of Tensile Properties of Heat-treated Ti-4A1-3Mo-1V Sheet
Author: H. R. Ogden
Publisher:
ISBN:
Category : Metals
Languages : en
Pages : 48
Book Description
Publisher:
ISBN:
Category : Metals
Languages : en
Pages : 48
Book Description
The Effect of Rate of Heating to Aging Temperature on the Tensile Properties of Ti-2.5Al-16V Alloy Sheet
Author: G. S. Root
Publisher:
ISBN:
Category : Titanium alloys
Languages : en
Pages : 16
Book Description
Publisher:
ISBN:
Category : Titanium alloys
Languages : en
Pages : 16
Book Description
Smooth and Sharpe-notch Property Variations for Several Heats of Ti-6A1-4V Sheet at Room and Cryogenic Temperatures
Author: Morgan P. Hanson
Publisher:
ISBN:
Category : Statistical matching
Languages : en
Pages : 22
Book Description
Publisher:
ISBN:
Category : Statistical matching
Languages : en
Pages : 22
Book Description
The Effect of Heat Treatment on the Tensile Properties of the Alloy Ti - 6 Al 4 V
Author: Jean-Michel DuPouy
Publisher:
ISBN:
Category :
Languages : en
Pages : 68
Book Description
Publisher:
ISBN:
Category :
Languages : en
Pages : 68
Book Description
TML Report
Author:
Publisher:
ISBN:
Category : Titanium
Languages : en
Pages : 304
Book Description
Publisher:
ISBN:
Category : Titanium
Languages : en
Pages : 304
Book Description
Review of Current Data on the Tensile Properties of Metals at Very Low Temperatures
Author: James Edward Campbell
Publisher:
ISBN:
Category : Liquid hydrogen
Languages : en
Pages : 90
Book Description
Publisher:
ISBN:
Category : Liquid hydrogen
Languages : en
Pages : 90
Book Description
T M L Report
Author: Battelle Memorial Institute. Titanium Metallurgical Laboratory
Publisher:
ISBN:
Category : Metallurgy
Languages : en
Pages : 92
Book Description
Publisher:
ISBN:
Category : Metallurgy
Languages : en
Pages : 92
Book Description
Hot Forming, Heat Treating, and Mechanical Evaluation of 4-Inch-Thick Ti-6Al-4V, ELI Plate
Author: Frank J. Lengenfelder
Publisher:
ISBN:
Category :
Languages : en
Pages : 21
Book Description
Elevated temperature tensile properties of the Ti-6Al-4V, ELI grade alloy were determined and a forming temperature range was selected. A 7-foot-diameter hemisphere was hot-press formed from a 4-inch-thick plate according to laboratory-developed parameters. Mechanical property tests were conducted on the plate material before and after hot forming and after heat treating of the formed material. Results of these tests showed a lower tensile yield strength after hot forming and restoration of this property after heat treatment. The results indicate that a tensile yield strength of 120,000 pounds per square inch can be obtained throughout the thickness of the formed hemisphere after appropriate heat treatment.
Publisher:
ISBN:
Category :
Languages : en
Pages : 21
Book Description
Elevated temperature tensile properties of the Ti-6Al-4V, ELI grade alloy were determined and a forming temperature range was selected. A 7-foot-diameter hemisphere was hot-press formed from a 4-inch-thick plate according to laboratory-developed parameters. Mechanical property tests were conducted on the plate material before and after hot forming and after heat treating of the formed material. Results of these tests showed a lower tensile yield strength after hot forming and restoration of this property after heat treatment. The results indicate that a tensile yield strength of 120,000 pounds per square inch can be obtained throughout the thickness of the formed hemisphere after appropriate heat treatment.