CARACTERISATION D'ALLIAGES LEGERS AL-CR-FE POUR APPLICATIONS A HAUTE TEMPERATURE ELABORES PAR SOLIDIFICATION RAPIDE PDF Download

Author: ABDELOUAHAB.. ZIANI
Publisher:
ISBN:
Category :
Languages : fr
Pages :

Get Book Here

Book Description
LA DEGRADATION DES PROPRIETES MECANIQUES A HAUTE TEMPERATURE EST RELIEE PRINCIPALEMENT A LA RECRISTALLISATION ET A LA COALESCENCE DES PRECIPITES. LA SOLUTION PROPOSEE POUR EVITER, OU LIMITER, CES PHENOMENES EST DE BLOQUER LES JOINTS DE GRAINS PAR DES DISPERSOIDES ET DE DURCIR LA MATRICE PAR DE PETITS PRECIPITES STABLES THERMIQUEMENT, DONT LES ELEMENTS SONT PEU SOLUBLES ET DIFFUSENT LENTEMENT DANS LA MATRICE. LES METAUX DE TRANSITION ET LES TERRES RARES VERIFIENT CES CONDITIONS. L'AMELIORATION DES PROPRIETES MECANIQUES PASSE PAR L'AUGMENTATION DE FRACTION VOLUMIQUE DES PRECIPITES, DONC PAR UNE AUGMENTATION DE LA TENEUR EN ELEMENTS D'ADDITION. COMPTE TENU DE LEUR FAIBLE SOLUBILITE DANS LA MATRICE IL EST NECESSAIRE DE RECOURIR AUX TECHNIQUES DE SOLIDIFICATION RAPIDE, EN L'OCCURRENCE LA PULVERISATION CENTRIFUGE. L'ALLIAGE FONDU EST COULE SUR UNE COUPELLE EN ROTATION (30000 TRS PAR MINUTE), LE FILM LIQUIDE SE SUBDIVISE EN FINES GOUTTELETTES (50-100 M DE DIAMETRE) QUI SE SOLIDIFIENT AVANT D'ATTEINDRE LES PAROIS DE L'ENCEINTE. LA POUDRE OBTENUE EST TAMISEE, DEGAZEE, PLACEE EN CONTENEUR ET EXTRUDEE A CHAUD. LES PROPRIETES MECANIQUES DES PRODUITS OBTENUS SONT MESUREES DANS L'ETAT BRUT OU APRES DES MAINTIENS A DIFFERENTES TEMPERATURES. CETTE ETUDE PRESENTE LES RESULTATS OBTENUS SUR DES ALLIAGES AL-CR-XFE (%AT) OU X VAUT 0, 1 ET 3. LES RESULTATS OBTENUS SERONT DISCUTES SUR LA BASE DE L'EVOLUTION DES MICROSTRUCTURES AVEC LES TEMPS ET TEMPERATURES DE MAINTIEN